Propiedades Mecanicas

Flowchart nodes

• Propiedades Mecanicas de los Materiales

• Acero 8620

• Polietileno de baja densidad

• Madera de pino

• Aluminio serie 2000

• Compuesto de matriz ceramica

• Metal puro

• Shear Modulus 38.1 GPa

• Poissons Ratio 0.29

• Poissons Ratio 0.29

• Machinability 65 %

• Reduction of Area 31 %

• Modulus of Elasticity 205 GPa

• Hardness, Rockwell B 80

• Hardness, Brinell: 149 

• Bulk Modulus 160 GPa

• Elongation at Break 31 %

• Hardness, Vickers 155

• Izod Impact 115 J

• Tensile Strength, Yield 385 MPa

• Tensile Strength, Ultimate 530 MPa

• Modulus of Elasticity 0.221 - 0.483 GPa

• Tensile Strength, Ultimate 11.0 - 14.0

• Hardness, Shore D 50.0 - 55.0

• Tensile Strength, Yield 10.0 - 14.0 MPa

• Elongation at Break 500 - 600 %

• Hardness, Wood Indentation 1800 N

• Work to Elastic Limit 0.00558 J/

• Tensile Strength, Ultimate 1.93 MPa

• Work to Maximum Load 0.0552 J/cm³

• Modulus of Rupture 0.0517 GPa

• Flexural Yield Strength 30.3 MPa

• Flexural Modulus 9.51 GPa

• Compressive Yield Strength 3.79 MPa

• Toughness 18.1 J

• Poissons Ratio 0.292

• Shear Strength 6.21 MPa

• Impact 3.1

• Hardness, Brinell 45.0 - 150

• Hardness, Knoop 72.0 - 191

• Tensile Strength, Ultimate 172 - 670 MPa

• Compressive Yield Strength 185 - 470 MPa

• Poissons Ratio 0.300 - 0.340

• Machinability 30.0 - 90.0 %

• Shear Strength 106 - 320 MPa

• Shear Modulus 26.0 - 44.2 GPa

• Fracture Toughness 19.0 - 49.0 MPa-m½

• Notched Tensile Strength 379 - 414 MP

• Modulus of Elasticity 70.0 - 115 GPa

• Creep Strength 315 - 470 MPa

• Elongation at Break 0.500 - 27.0 %

• Tensile Stress 34.5 MPa

• Tensile Modulus 31.0 GP

• Tensile Strength 124 MP

• Shear Strength 9.00 MPa

• Hardness, Vickers 65

• Tensile Strength, Ultimate 240 MPa

• Shear Modulus 38.1 GPa

• Poissons Ratio 0.35

• Tensile Strength, Yield 170 MPa

• Elongation at Break 50 %

• Modulus of Elasticity 103 GPa